CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
Cu(1) | Al | Sb | Fe | Pb | Ni(2) | P(3) | Si | S | Sn | Zn | |
Min./Max. | 81.0-85.0 | .005 | .35 | .20 | 6.0-8.0 | 1.0 | .15 | .005 | .08 | 6.3-7.5 | 1.0-4.0 |
Nominal | 83.0 | - | - | - | 7.0 | - | - | - | - | 6.9 | 2.5 |
MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
Temper | Section Size |
Cold Work |
Typ/ Min |
Temp | Tensile Strength |
Yield Strength (0.5% ext. under load) |
El | Rockwell Hardness |
Brinell Hard. |
Fatigue Strength* |
|
||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
in. | % | F | ksi | ksi | % | B | C | F | 30T | 500 | 3000 | ksi | |||||||
mm. | C | MPa | MPa | MPa | |||||||||||||||
As Sand Cast | |||||||||||||||||||
M01 | 0.0 | 0 | TYP | 68 | 35 | 18 | 20 | - | - | - | - | 65 | - | 16 | |||||
0.0 | 20 | 241 | 124 | 20 | - | - | - | - | 65 | - | 110 | ||||||||
As Centrifugal Cast | |||||||||||||||||||
M02 | 0.0 | 0 | SMIN | 68 | 30 | 14 | 15 | - | - | - | - | - | - | - | |||||
0.0 | 20 | 207 | 97 | 15 | - | - | - | - | - | - | - | ||||||||
As Continuous Cast | |||||||||||||||||||
M07 | 0.0 | 0 | SMIN | 68 | 35 | 20 | 10 | - | - | - | - | - | - | - | |||||
0.0 | 20 | 241 | 138 | 10 | - | - | - | - | - | - | - | ||||||||
As Sand Cast | |||||||||||||||||||
M01 | 0.0 | 0 | SMIN | 68 | 30 | 14 | 15 | - | - | - | - | - | - | - | |||||
0.0 | 20 | 207 | 97 | 15 | - | - | - | - | - | - | - | ||||||||
Product | Specification | |
Centrifugal | ASTM B271 SAE J462, J461 |
|
Continuous | ASTM B505 SAE J461, J462 |
|
Ingot | ASTM B30 | |
Permanent Mold | SAE J461, J462 | |
Sand | ASTM B584, B763, B66 SAE J462, J461 |